priti®multibloc ZrO2 multicolor

Order number: 220881
priti®multibloc ZrO2 multicolor
priti®multibloc ZrO2 multicolor
priti®multibloc ZrO2 multicolor
     
Image can differ
Description

49 % translucence, multicolor – Material of choice for aesthetic, fully anatomical, monolithic restorations with up to three pontics.

Note

For the purchase of this product please contact our service team

Request offer
Order number: 220881
For aesthetic, fully anatomical, monolithic restorations with up to three pontics.... more
Product information "priti®multibloc ZrO2 multicolor"

For aesthetic, fully anatomical, monolithic restorations with up to three pontics.
priti®multibloc ZrOmulticolor High Translucent is the material of choice for aesthetic, fully anatomical, monolithic restorations with up to three pontics. For an ultimate, vibrant aesthetic with 49 % translucence, >650 MPa flexural strength, integrated color gradient

Indication:
You can use priti®multibloc ZrOmulticolor High Translucent to fabricate inlays, onlays, veneers, partial crowns, anatomically reduced and monolithic, fully anatomical crowns and bridges (up to three pontics) for anterior and posterior areas Translucence is comparable to that of lithium disilicate. Its high translucence and integrated color gradient mean the material is particularly suitable for efficient fabrication of non-veneered restorations.

Material:

  • Zirconium dioxide Type II, Class 4 (DIN EN ISO 6872)
  • High strength > 650 MPa
  • Very high translucence, 49%, comparable with
  • Brilliant aesthetics
  • CTE 10 -6 K-1
  • Thin wall thicknesses of 0.4 mm for single crowns in the anterior tooth area and 0.6 mm in the posterior tooth area
  • Precise edges and margins due to highly compacted material
  • Veneering possible with any ceramic mapped to the CTE of ZrO2
  • Cross-batch color fidelity
  • Homogeneous block shading
  • Color can be reproduced at any time
  • Biocompatible

Chemical Composition:

Zirconium dioxide (ZrO2/HfO2): 89.89 - 90.7 %
Yttrium oxide (Y2O3): 8.55 - 10.11 %
Aluminum oxide (Al2O3): < 0.2 %
Other oxides: < 0.7 %

Shape: Blöcke
Needle diameter: Zirkoniumdioxid