Tizian Blank NEM fine 98 mm
Product number:
220279
Questions about the product? We are glad to be here for you!
Product information "Tizian Blank NEM fine 98 mm"
Tizian Blanks NEM (non-precious metal) are made of beryllium-free and cadmium-free CoCr ceramic alloy according to DIN EN OSP 22674 and EN ISO 9693 for applications with thin cross-sections which are exposed to extreme forces. Examples are removable partial dentures, clasps, thin veneered individual crowns, fixed full arch dentures or bridges with small cross-sections, bars, fixations, implant-supported supraconstructions.
Properties:
Alloy type: 4
Density: 8.8 g/cm³
Vickers hardness: 285 HV 10/30
CTE- value (25-500 °C): 14,4*10-6 K-1
Oxidation without vacuum (Point 4c): 1000 °C
Mass content of the components (in weight-%)*: Co 63, Cr 29, Mo 6 / Mn x, Nb x, Si x, Fe x
Tensile strength: 680 MPa
0.2 % yield point: 400 MPa
Elongation at break: 9 %
E-module: 250 GPa
*X= <, 1%
Cutsomers also bought
Tizian Blank NEM fine 98 mm
Tizian Blanks NEM (non-precious metal) are made of beryllium-free and cadmium-free CoCr ceramic alloy according to DIN EN OSP 22674 and EN ISO 9693 for applications with thin cross-sections which are exposed to extreme forces. Examples are removable partial dentures, clasps, thin veneered individual crowns, fixed full arch dentures or bridges with small cross-sections, bars, fixations, implant-supported supraconstructions. Properties: Alloy type: 4Density: 8.8 g/cm³Vickers hardness: 285 HV 10/30CTE- value (25-500 °C): 14,4*10-6 K-1Oxidation without vacuum (Point 4c): 1000 °CMass content of the components (in weight-%)*: Co 63, Cr 29, Mo 6 / Mn x, Nb x, Si x, Fe xTensile strength: 680 MPa0.2 % yield point: 400 MPaElongation at break: 9 %E-module: 250 GPa *X= <, 1%
Tizian Blank NEM fine 98 mm
Tizian Blanks NEM (non-precious metal) are made of beryllium-free and cadmium-free CoCr ceramic alloy according to DIN EN OSP 22674 and EN ISO 9693 for applications with thin cross-sections which are exposed to extreme forces. Examples are removable partial dentures, clasps, thin veneered individual crowns, fixed full arch dentures or bridges with small cross-sections, bars, fixations, implant-supported supraconstructions. Properties: Alloy type: 4Density: 8.8 g/cm³Vickers hardness: 285 HV 10/30CTE- value (25-500 °C): 14,4*10-6 K-1Oxidation without vacuum (Point 4c): 1000 °CMass content of the components (in weight-%)*: Co 63, Cr 29, Mo 6 / Mn x, Nb x, Si x, Fe xTensile strength: 680 MPa0.2 % yield point: 400 MPaElongation at break: 9 %E-module: 250 GPa *X= <, 1%
T61 Tizian Cut 5/3.5 radius cutter 3.0 mm for Titan/CoCr, 4-bladed, 6 mm shaft
T61 - metal roughing tool The complex geometry of the four high-capacity cutting edges (this is not a radius cutter!) facilitate a smooth operation, a much better service life and time savings of up to 50 % during the roughing procedure. Metal restorations are manufactured within ca. 10-15 min. in extraordinary quality. Please note that the special cutter geometry requires a new strategy and new tool data in the CAM software. This tool does not replace the reliable T6! Diameter Ø 3.0 mm Cutting edges quadruple edge Shaft Ø 6 mm Cutting length: l = 15 mm Total length: 45 mm Max. blank height: 15 mm Blank material: CoCr, titanium Coating type: coated For milling machines: Tizian Cut 5.2 Series, Tizian Cut 5, CORiTEC 550i, CORiTEC 750i
Tizian Blank NEM fine 98 mm
Tizian Blanks NEM (non-precious metal) are made of beryllium-free and cadmium-free CoCr ceramic alloy according to DIN EN OSP 22674 and EN ISO 9693 for applications with thin cross-sections which are exposed to extreme forces. Examples are removable partial dentures, clasps, thin veneered individual crowns, fixed full arch dentures or bridges with small cross-sections, bars, fixations, implant-supported supraconstructions. Properties: Alloy type: 4Density: 8.8 g/cm³Vickers hardness: 285 HV 10/30CTE- value (25-500 °C): 14,4*10-6 K-1Oxidation without vacuum (Point 4c): 1000 °CMass content of the components (in weight-%)*: Co 63, Cr 29, Mo 6 / Mn x, Nb x, Si x, Fe xTensile strength: 680 MPa0.2 % yield point: 400 MPaElongation at break: 9 %E-module: 250 GPa *X= <, 1%
Tizian Blank NEM fine 98 mm
Tizian Blanks NEM (non-precious metal) are made of beryllium-free and cadmium-free CoCr ceramic alloy according to DIN EN OSP 22674 and EN ISO 9693 for applications with thin cross-sections which are exposed to extreme forces. Examples are removable partial dentures, clasps, thin veneered individual crowns, fixed full arch dentures or bridges with small cross-sections, bars, fixations, implant-supported supraconstructions. Properties: Alloy type: 4Density: 8.8 g/cm³Vickers hardness: 285 HV 10/30CTE- value (25-500 °C): 14,4*10-6 K-1Oxidation without vacuum (Point 4c): 1000 °CMass content of the components (in weight-%)*: Co 63, Cr 29, Mo 6 / Mn x, Nb x, Si x, Fe xTensile strength: 680 MPa0.2 % yield point: 400 MPaElongation at break: 9 %E-module: 250 GPa *X= <, 1%
Tizian Blank NEM fine 98 mm
Tizian Blanks NEM (non-precious metal) are made of beryllium-free and cadmium-free CoCr ceramic alloy according to DIN EN OSP 22674 and EN ISO 9693 for applications with thin cross-sections which are exposed to extreme forces. Examples are removable partial dentures, clasps, thin veneered individual crowns, fixed full arch dentures or bridges with small cross-sections, bars, fixations, implant-supported supraconstructions. Properties: Alloy type: 4Density: 8.8 g/cm³Vickers hardness: 285 HV 10/30CTE- value (25-500 °C): 14,4*10-6 K-1Oxidation without vacuum (Point 4c): 1000 °CMass content of the components (in weight-%)*: Co 63, Cr 29, Mo 6 / Mn x, Nb x, Si x, Fe xTensile strength: 680 MPa0.2 % yield point: 400 MPaElongation at break: 9 %E-module: 250 GPa *X= <, 1%