Tizian Blank PMMA 98 x 20 mm, Color: A2

Aesthetics and durability combined to create a true multi-talent. The wonderful result of a merger between stability and natural beauty.Our new multi-talent is the ideal product to support you along your individual path to highly aesthetic and durable dental restorations. This blank follows the trend to combine the positive features of the already established zirconium quality of 3Y-TZP and the highly translucent 5Y-TZP. Just imagine mixing two different material classes... What could result from it is a unique raw material combination of a high-strength and highly translucent ZrO2. We just did it! When adding our new and innovative TILLY philosophy, the result was a multi-talented product which defines a completely new generation! Produce individual restorations for the anterior and posterior sector on natural tooth stumps and implants with priti®multidisc ZrO2 Multi Translucent.The special feature: graduation of shade and translucency with a simultaneous high flexural strength. These characteristics make priti®multidisc ZrO2 Multi Translucent an extraordinary and flexible choice for a wide range of indications.Benefits Excellent dental aesthetics Naturally graduated shade and translucency High stability: flexural strength >, 1,100 MPa (typical average) All processing techniques: painting technique, cut-back technique, veneering technique Quick sintering, complete processing time ca. 4 hours, released for up to 3 unit restorations High translucency in the incisal sector (>, 49 %), mechanical load capacity in the dentin sector Which is technique is your favorite?Select from these techniques: painting technique, cut-back technique, veneering technique. Indications: Individual restorations for the anterior and posterior sector on natural tooth stumps and implants  Highly aesthetic monolithic fully anatomic crowns, partial crowns and bridges of up to 14 units Inlays, onlays, veneers and abutments Quick sintering of restorations with up to 3 units Facts: Zirkonium dioxide type II, class 5 accordingt to DIN EN ISO 6872 Flexural strength: typical average ? 1,100 MPa Translucency graduation of <, 40 % to >, 49 % Thin wall thickness, in the anterior sector 0.4 mm and in the posterior sector 0.6 mm for individual crowns Precise margins and edges due to high density material Can be veneered with all ceramics which are adapted to the CTE of 10 · 10-6 · K-1 von ZrO2  Color stability across the batches Homogeneous coloration Reproducible colors Biocompatible  

The tooth-colored Tizian Blanks PMMA are suited to the production of crowns and bridges as long-term temporaries. The advantage of these tooth-colored resin blanks is their excellent physical properties. All Tizian Blanks PMMA can be used with or without veneers. In addition, it is possible to check fit and function of the restorations on a plaster model. Indications: Long-term temporaries (up to 6 months), suited to veneering with composite.

Aesthetics and durability combined to create a true multi-talent. The wonderful result of a merger between stability and natural beauty.Our new multi-talent is the ideal product to support you along your individual path to highly aesthetic and durable dental restorations. This blank follows the trend to combine the positive features of the already established zirconium quality of 3Y-TZP and the highly translucent 5Y-TZP. Just imagine mixing two different material classes... What could result from it is a unique raw material combination of a high-strength and highly translucent ZrO2. We just did it! When adding our new and innovative TILLY philosophy, the result was a multi-talented product which defines a completely new generation! Produce individual restorations for the anterior and posterior sector on natural tooth stumps and implants with priti®multidisc ZrO2 Multi Translucent.The special feature: graduation of shade and translucency with a simultaneous high flexural strength. These characteristics make priti®multidisc ZrO2 Multi Translucent an extraordinary and flexible choice for a wide range of indications.Benefits Excellent dental aesthetics Naturally graduated shade and translucency High stability: flexural strength >, 1,100 MPa (typical average) All processing techniques: painting technique, cut-back technique, veneering technique Quick sintering, complete processing time ca. 4 hours, released for up to 3 unit restorations High translucency in the incisal sector (>, 49 %), mechanical load capacity in the dentin sector Which is technique is your favorite?Select from these techniques: painting technique, cut-back technique, veneering technique. Indications: Individual restorations for the anterior and posterior sector on natural tooth stumps and implants  Highly aesthetic monolithic fully anatomic crowns, partial crowns and bridges of up to 14 units Inlays, onlays, veneers and abutments Quick sintering of restorations with up to 3 units Facts: Zirkonium dioxide type II, class 5 accordingt to DIN EN ISO 6872 Flexural strength: typical average ? 1,100 MPa Translucency graduation of <, 40 % to >, 49 % Thin wall thickness, in the anterior sector 0.4 mm and in the posterior sector 0.6 mm for individual crowns Precise margins and edges due to high density material Can be veneered with all ceramics which are adapted to the CTE of 10 · 10-6 · K-1 von ZrO2  Color stability across the batches Homogeneous coloration Reproducible colors Biocompatible  

The tooth-colored Tizian Blanks PMMA are suited to the production of crowns and bridges as long-term temporaries. The advantage of these tooth-colored resin blanks is their excellent physical properties. All Tizian Blanks PMMA can be used with or without veneers. In addition, it is possible to check fit and function of the restorations on a plaster model. Indications: Long-term temporaries (up to 6 months), suited to veneering with composite.

Tizian Blank PMMA Splint is made of a highly pure themoplastic PMMA which is produced following the highest quality standards. The crystal clear, color-stable material stands out with its homogeneity, low plaque adhesion and low water absorption. Tizian Blank PMMA Splint is an economic alternative for the splint technology. It can be be repaired and extended with PMMA acrylics. Indications: Occlusion splints Drilling templates for navigated implantation Lost wax technique in casting technology Processing: Due to the chemical and physical properties of thermoplastic PMMA, there is a risk of melting the material during dry machining and thus smearing the mills. Therefore, it is important to use only single-edged mills. If necessary, the milling strategy must be adjusted with a slower cutting speed and a lower feed rate. The material can be processed by wet machining with PMMA mills in a standard strategy without restrictions. 

Specially designed for the production of splints Tizian flex splint comfort blanks have been developed for the production of dental splints with thermal effect. They stand out by their thermoplastic flexibility which lets the user achieve a highly precise fit to the individual dental situation. These characteristics ensure an exceptional and stressless wearing comfort for the patients. What's more, the self-adjusting Tizian flex splint comfort splints are extremely break-resistant and have a high transparency. An extraordinary material homogeneity is achieved by means of an industrial polymerization process. This guarantees an outstanding long-term stability. Processing the Tizian flex splint comfort blanks with CAD/CAM technology further ensures a safe procedure, since mixing errors (e.g. by manual mixing) are eliminated. In addition, the odors which occur during mixing are avoided. Your benefits: High transparency Extremely break-resistant and long-term stable Extraordinary wearing comfort for your patients free of MMA and BPO Safe procedure by means of CAD/CAM technology Indications: Therapeutic splints Reflex splints Stabilization splints Positioning splints Composition: <, 10 % 1,2-cyclohexanedicarboxylic acid diisononyl ester >, 90 % poly(m)ethyl methacrylate, homopolymer