Tizian Blank PMMA Splint 98 mm
Advantages
- Economic alternative for the splint technology
- Crystal clear, color-stable and homogeneous
- Low plaque adhesion and low water absorption
Properties
Technical properties
Bending strength: 156 ± 6 MPa
Flexural modulus: 3000 ± 100 MPa
Glass transition temperature: 121 °C
Vickers hardness: 23.2 ± 0.3 HV 0,2
Water absorption: < 32 µg / mm'
Water solubility: < 1.6 µg / mm'
Description
Crystal clear, color-stable and homogeneous. Made from highly pure thermoplastic PMMA - the economic alternative for the splint technology
Tizian Blank PMMA Splint is made of a highly pure themoplastic PMMA which is produced following the highest quality standards. The crystal clear, color-stable material stands out with its homogeneity, low plaque adhesion and low water absorption. Tizian Blank PMMA Splint is an economic alternative for the splint technology. It can be be repaired and extended with PMMA acrylics.
Indications:
- Occlusion splints
- Drilling templates for navigated implantation
- Lost wax technique in casting technology
Processing:
Due to the chemical and physical properties of thermoplastic PMMA, there is a risk of melting the material during dry machining and thus smearing the mills. Therefore, it is important to use only single-edged mills. If necessary, the milling strategy must be adjusted with a slower cutting speed and a lower feed rate. The material can be processed by wet machining with PMMA mills in a standard strategy without restrictions.