Tizian Block 5.0 Multilayer 5YZirconia, High Translucent, B light, 3 pieces
Description
Material of choice for aesthetic, fully anatomical, monolithic restorations with up to three pontics.
For aesthetic, fully anatomical, monolithic restorations with up to three pontics.
Tizian Block 5.0 Multilayer 5YZirconia is the material of choice for aesthetic, fully anatomical, monolithic restorations with up to three pontics. For an ultimate, vibrant aesthetic with 49% translucence, >,650 MPa flexural strength, integrated color gradient
Indication:
You can use Tizian Block 5.0 Multilayer 5YZirconia to fabricate inlays, onlays, veneers, partial crowns, anatomically reduced and monolithic, fully anatomical crowns and bridges (up to three pontics) for anterior and posterior areas Translucence is comparable to that of lithium disilicate. Its high translucence and integrated color gradient mean the material is particularly suitable for efficient fabrication of non-veneered restorations.
Material:
- Zirconium dioxide Type II, Class 4 (DIN EN ISO 6872)
- High strength >, 650 MPa
- Very high translucence, 49%, comparable with
- Brilliant aesthetics
- CTE 10 -6 K-1
- Thin wall thicknesses of 0.4 mm for single crowns in the anterior tooth area and 0.6 mm in the posterior tooth area
- Precise edges and margins due to highly compacted material
- Veneering possible with any ceramic mapped to the CTE of ZrO2
- Cross-batch color fidelity
- Homogeneous block shading
- Color can be reproduced at any time
- Biocompatible
Chemical Composition:
Zirconium dioxide (ZrO2/HfO2): 89.89 - 90.7 %
Yttrium oxide (Y2O3): 8.55 - 10.11 %
Aluminum oxide (Al2O3): <, 0.2 %
Other oxides: <, 0.7 %