priti®multidisc ZrO2 Opaque, 98x 20, Colour A2

Advantages

  • Very aesthetic: 35 % translucency
  • Consistent color results
  • Biocompatible

Properties

  • Monolithic, fully anatomical (partial) crowns, bridges with up to 16-units, frameworks    
  • Recommended for covering discolored tooth stumps or metal structures

Description

35 % translucency – Brilliant results with the next generation zirconium dioxide.

Product number: 220667
Questions about the product? We are glad to be here for you!
Product information "priti®multidisc ZrO2 Opaque, 98x 20, Colour A2"

With a translucency of 35 %.

Indications:  

  • Very aesthetic monolithic, fully anatomical crowns, partial crowns and bridges with up to 16-units, frameworks    
  • Recommended for covering discolored tooth stumps or metal structures

Advantages of monochromatic precolored blanks

Why use precolored material? Applying a penetrating, homogeneous stain to the material does away with the need for processes such as dipping, painting and drying. This does not only save time and effort, but it also helps to avoid potential manual errors during the staining process. This reduces production costs and your customers will appreciate the consistent and reproducible color quality. Since the material comes fully precolored, even finishing or adjustment grinding do not leave light spots, which would have a negative effect on the appearance of the finished product.

Industrially precolored zirconium blanks are reproducible. Precolored material is gentle on your sintering furnace and protects its components from damage. Acid-based liquid stains can emit fumes during the sintering process which leave deposits on the the heating elements of the furnace and contaminate them. This can cause undesirable discoloration and/or loss of translucency. Using industrially precolored zirconium ensures consistent color results.

Suitable for:

  • open milling system with a blank holder for round blanks with a diameter of 98.5 mm


Material:  

  • Zirconium type II, class 5 according to DIN EN ISO 6872  
  • Good flexural strength of >, 1,150 MPa  
  • Very high translucency of 35 %
  • Good aging resistance
  • Thin wall thicknesses for single crowns in the anterior tooth area 0.4 mm and in the posterior tooth area 0.6 mm  
  • Biocompatible

 

 

Cutsomers also bought

priti®multidisc ZrO2 Opaque, 98 mm
With a translucency of 35 %.Indications:   Very aesthetic monolithic, fully anatomical crowns, partial crowns and bridges with up to 16-units, frameworks     Recommended for covering discolored tooth stumps or metal structures Advantages of monochromatic precolored blanks Why use precolored material? Applying a penetrating, homogeneous stain to the material does away with the need for processes such as dipping, painting and drying. This does not only save time and effort, but it also helps to avoid potential manual errors during the staining process. This reduces production costs and your customers will appreciate the consistent and reproducible color quality. Since the material comes fully precolored, even finishing or adjustment grinding do not leave light spots, which would have a negative effect on the appearance of the finished product. Industrially precolored zirconium blanks are reproducible. Precolored material is gentle on your sintering furnace and protects its components from damage. Acid-based liquid stains can emit fumes during the sintering process which leave deposits on the the heating elements of the furnace and contaminate them. This can cause undesirable discoloration and/or loss of translucency. Using industrially precolored zirconium ensures consistent color results. Suitable for: open milling system with a blank holder for round blanks with a diameter of 98.5 mm Material:   Zirconium type II, class 5 according to DIN EN ISO 6872   Good flexural strength of >, 1,150 MPa   Very high translucency of 35 % Good aging resistance Thin wall thicknesses for single crowns in the anterior tooth area 0.4 mm and in the posterior tooth area 0.6 mm   Biocompatible    
Details
priti®multidisc ZrO2 Multi Translucent 98 x 16 mm, Colour A1
Aesthetics and durability combined to create a true multi-talent. The wonderful result of a merger between stability and natural beauty.Our new multi-talent is the ideal product to support you along your individual path to highly aesthetic and durable dental restorations. This blank follows the trend to combine the positive features of the already established zirconium quality of 3Y-TZP and the highly translucent 5Y-TZP. Just imagine mixing two different material classes... What could result from it is a unique raw material combination of a high-strength and highly translucent ZrO2. We just did it! When adding our new and innovative TILLY philosophy, the result was a multi-talented product which defines a completely new generation! Produce individual restorations for the anterior and posterior sector on natural tooth stumps and implants with priti®multidisc ZrO2 Multi Translucent.The special feature: graduation of shade and translucency with a simultaneous high flexural strength. These characteristics make priti®multidisc ZrO2 Multi Translucent an extraordinary and flexible choice for a wide range of indications.Benefits Excellent dental aesthetics Naturally graduated shade and translucency High stability: flexural strength >, 1,100 MPa (typical average) All processing techniques: painting technique, cut-back technique, veneering technique Quick sintering, complete processing time ca. 4 hours, released for up to 3 unit restorations High translucency in the incisal sector (>, 49 %), mechanical load capacity in the dentin sector Which is technique is your favorite?Select from these techniques: painting technique, cut-back technique, veneering technique. Indications: Individual restorations for the anterior and posterior sector on natural tooth stumps and implants  Highly aesthetic monolithic fully anatomic crowns, partial crowns and bridges of up to 14 units Inlays, onlays, veneers and abutments Quick sintering of restorations with up to 3 units Facts: Zirkonium dioxide type II, class 5 accordingt to DIN EN ISO 6872 Flexural strength: typical average ? 1,100 MPa Translucency graduation of <, 40 % to >, 49 % Thin wall thickness, in the anterior sector 0.4 mm and in the posterior sector 0.6 mm for individual crowns Precise margins and edges due to high density material Can be veneered with all ceramics which are adapted to the CTE of 10 · 10-6 · K-1 von ZrO2  Color stability across the batches Homogeneous coloration Reproducible colors Biocompatible  
Details
priti®multidisc ZrO2 Multi Translucent 98 x 16 mm, Colour A3
Aesthetics and durability combined to create a true multi-talent. The wonderful result of a merger between stability and natural beauty.Our new multi-talent is the ideal product to support you along your individual path to highly aesthetic and durable dental restorations. This blank follows the trend to combine the positive features of the already established zirconium quality of 3Y-TZP and the highly translucent 5Y-TZP. Just imagine mixing two different material classes... What could result from it is a unique raw material combination of a high-strength and highly translucent ZrO2. We just did it! When adding our new and innovative TILLY philosophy, the result was a multi-talented product which defines a completely new generation! Produce individual restorations for the anterior and posterior sector on natural tooth stumps and implants with priti®multidisc ZrO2 Multi Translucent.The special feature: graduation of shade and translucency with a simultaneous high flexural strength. These characteristics make priti®multidisc ZrO2 Multi Translucent an extraordinary and flexible choice for a wide range of indications.Benefits Excellent dental aesthetics Naturally graduated shade and translucency High stability: flexural strength >, 1,100 MPa (typical average) All processing techniques: painting technique, cut-back technique, veneering technique Quick sintering, complete processing time ca. 4 hours, released for up to 3 unit restorations High translucency in the incisal sector (>, 49 %), mechanical load capacity in the dentin sector Which is technique is your favorite?Select from these techniques: painting technique, cut-back technique, veneering technique. Indications: Individual restorations for the anterior and posterior sector on natural tooth stumps and implants  Highly aesthetic monolithic fully anatomic crowns, partial crowns and bridges of up to 14 units Inlays, onlays, veneers and abutments Quick sintering of restorations with up to 3 units Facts: Zirkonium dioxide type II, class 5 accordingt to DIN EN ISO 6872 Flexural strength: typical average ? 1,100 MPa Translucency graduation of <, 40 % to >, 49 % Thin wall thickness, in the anterior sector 0.4 mm and in the posterior sector 0.6 mm for individual crowns Precise margins and edges due to high density material Can be veneered with all ceramics which are adapted to the CTE of 10 · 10-6 · K-1 von ZrO2  Color stability across the batches Homogeneous coloration Reproducible colors Biocompatible  
Details
Cooling lubricant 1.000 ml, biocompatible, für Tizian Cut 5 and Tizian 3.5
Use this cooling lubricant for your Tizian Cut 5 or Tizian Cut 5.2.
Details
Tizian Blank NEM fine 98 mm
Tizian Blanks NEM (non-precious metal) are made of beryllium-free and cadmium-free CoCr ceramic alloy according to DIN EN OSP 22674 and EN ISO 9693 for applications with thin cross-sections which are exposed to extreme forces. Examples are removable partial dentures, clasps, thin veneered individual crowns, fixed full arch dentures or bridges with small cross-sections, bars, fixations, implant-supported supraconstructions. Properties: Alloy type: 4Density: 8.8 g/cm³Vickers hardness: 285 HV 10/30CTE- value (25-500 °C): 14,4*10-6 K-1Oxidation without vacuum (Point 4c): 1000 °CMass content of the components (in weight-%)*: Co 63, Cr 29, Mo 6 / Mn x, Nb x, Si x, Fe xTensile strength: 680 MPa0.2 % yield point: 400 MPaElongation at break: 9 %E-module: 250 GPa *X= <, 1%
Details
priti®multidisc ZrO2 Opaque, 98x 20, Colour A3,5
With a translucency of 35 %.Indications:   Very aesthetic monolithic, fully anatomical crowns, partial crowns and bridges with up to 16-units, frameworks     Recommended for covering discolored tooth stumps or metal structures Advantages of monochromatic precolored blanks Why use precolored material? Applying a penetrating, homogeneous stain to the material does away with the need for processes such as dipping, painting and drying. This does not only save time and effort, but it also helps to avoid potential manual errors during the staining process. This reduces production costs and your customers will appreciate the consistent and reproducible color quality. Since the material comes fully precolored, even finishing or adjustment grinding do not leave light spots, which would have a negative effect on the appearance of the finished product. Industrially precolored zirconium blanks are reproducible. Precolored material is gentle on your sintering furnace and protects its components from damage. Acid-based liquid stains can emit fumes during the sintering process which leave deposits on the the heating elements of the furnace and contaminate them. This can cause undesirable discoloration and/or loss of translucency. Using industrially precolored zirconium ensures consistent color results. Suitable for: open milling system with a blank holder for round blanks with a diameter of 98.5 mm Material:   Zirconium type II, class 5 according to DIN EN ISO 6872   Good flexural strength of >, 1,150 MPa   Very high translucency of 35 % Good aging resistance Thin wall thicknesses for single crowns in the anterior tooth area 0.4 mm and in the posterior tooth area 0.6 mm   Biocompatible    
Details