priti®perfect transpa-blue,

Tizian Blanks NEM (non-precious metal) are made of beryllium-free and cadmium-free CoCr ceramic alloy according to DIN EN OSP 22674 and EN ISO 9693 for applications with thin cross-sections which are exposed to extreme forces. Examples are removable partial dentures, clasps, thin veneered individual crowns, fixed full arch dentures or bridges with small cross-sections, bars, fixations, implant-supported supraconstructions. Properties: Alloy type: 4Density: 8.8 g/cm³Vickers hardness: 285 HV 10/30CTE- value (25-500 °C): 14,4*10-6 K-1Oxidation without vacuum (Point 4c): 1000 °CMass content of the components (in weight-%)*: Co 63, Cr 29, Mo 6 / Mn x, Nb x, Si x, Fe xTensile strength: 680 MPa0.2 % yield point: 400 MPaElongation at break: 9 %E-module: 250 GPa *X= <, 1%

priti® perfectKeep it simple! priti®perfect stands for: Stability of the color effect from the model to the mouth. It is easy to keep control with brush technique and the pasty masses. The final color shows already during application. priti®perfect aims at the single firing solution with only 20 components. Nevertheless, depending on the case, the double firing solution or internal staining is also an option. The perfect finish pritidenta is at your side with intelligent solutions from determining the shade to the insertion of the restoration. Mill teeth from multicolor material, sinter them and finalizing them aesthetically! This is simple, fast, first-class and therefore already masterful! priti®perfect gives the existing priti® concept the very last finishing touch. This is sophisticated perfection for aesthetics! Your benefits: Highly aesthetic colors, with only 20 components - final colors already visible during application Effective design: single firing solution preferred Released for: Zirconium dioxide Monolithic zirconium dioxide Layered ceramics for zirconium dioxide Layered ceramics for metals Lithium disilicate

Tizian Blanks NEM (non-precious metal) are made of beryllium-free and cadmium-free CoCr ceramic alloy according to DIN EN OSP 22674 and EN ISO 9693 for applications with thin cross-sections which are exposed to extreme forces. Examples are removable partial dentures, clasps, thin veneered individual crowns, fixed full arch dentures or bridges with small cross-sections, bars, fixations, implant-supported supraconstructions. Properties: Alloy type: 4Density: 8.8 g/cm³Vickers hardness: 285 HV 10/30CTE- value (25-500 °C): 14,4*10-6 K-1Oxidation without vacuum (Point 4c): 1000 °CMass content of the components (in weight-%)*: Co 63, Cr 29, Mo 6 / Mn x, Nb x, Si x, Fe xTensile strength: 680 MPa0.2 % yield point: 400 MPaElongation at break: 9 %E-module: 250 GPa *X= <, 1%

Tizian Blanks NEM (non-precious metal) are made of beryllium-free and cadmium-free CoCr ceramic alloy according to DIN EN OSP 22674 and EN ISO 9693 for applications with thin cross-sections which are exposed to extreme forces. Examples are removable partial dentures, clasps, thin veneered individual crowns, fixed full arch dentures or bridges with small cross-sections, bars, fixations, implant-supported supraconstructions. Properties: Alloy type: 4Density: 8.8 g/cm³Vickers hardness: 285 HV 10/30CTE- value (25-500 °C): 14,4*10-6 K-1Oxidation without vacuum (Point 4c): 1000 °CMass content of the components (in weight-%)*: Co 63, Cr 29, Mo 6 / Mn x, Nb x, Si x, Fe xTensile strength: 680 MPa0.2 % yield point: 400 MPaElongation at break: 9 %E-module: 250 GPa *X= <, 1%

priti® perfectKeep it simple! priti®perfect stands for: Stability of the color effect from the model to the mouth. It is easy to keep control with brush technique and the pasty masses. The final color shows already during application. priti®perfect aims at the single firing solution with only 20 components. Nevertheless, depending on the case, the double firing solution or internal staining is also an option. The perfect finish pritidenta is at your side with intelligent solutions from determining the shade to the insertion of the restoration. Mill teeth from multicolor material, sinter them and finalizing them aesthetically! This is simple, fast, first-class and therefore already masterful! priti®perfect gives the existing priti® concept the very last finishing touch. This is sophisticated perfection for aesthetics! Your benefits: Highly aesthetic colors, with only 20 components - final colors already visible during application Effective design: single firing solution preferred Released for: Zirconium dioxide Monolithic zirconium dioxide Layered ceramics for zirconium dioxide Layered ceramics for metals Lithium disilicate

Tizian Blanks NEM are made from a biocompatible non-precious alloy on CoCr basis. The blanks are free of nickel and beryllium. Mill your crowns and bridges from Tizian Blanks NEM. Specifically well suited bonding oxide formers ensure an optimal metal ceramic bond. Its Vickers hardness of 320 HV10 makes the CoCr material easy to mill and to polish. Indcations: Crowns and bridges to be veneered with ceramics Inlays and onlays Abutments Special restorations such as cantilever bridges or attachment parts: responsibility of the attending dentist (evaluation ot the responsibility) Your benefits: Homogenous quality Excellent surface quality Ideal Vickers hardness (275 HV10) Free of molybdenum for a smooth for a smooth movement of the telescopic crowns Clean material removal for a long service-life of the mills Stable...