Micronium N10, 1 kg, CoCrMo alloy
Description
This CoCr based model cast alloy is ideally suited for clamp frameworks due to its E modulus.
Product number:
610120
Questions about the product? We are glad to be here for you!
Product information "Micronium N10, 1 kg, CoCrMo alloy"
CoCr alloy specially for your delicate clamp frameworks.
,
Benefits:
- Extremely high elongation at break (11%)
- Extremely high tensile strength (1680 N/mm 2)
- Easily removed oxide
- High level of safety and long life span
- Very high spring stiffness - particularly important for clamps
- Very good activation
,
Physical attributes:
- Hardness: HV 340
- Elongation at break: 11 %
- Tensile strength: 1.680 µPa
- Specific weight: 8.4 g/cm2
- Melting range: 1343-1398 °C
Brochures and further information on this product
Cutsomers also bought
Laser welding wire, CoCr, 0.35 mm round, 0.35 mm round
For safe welding of your CoCr technical dental work using the laser and plasma welding technique.
Tizian Blank NEM fine 98 mm
Tizian Blanks NEM (non-precious metal) are made of beryllium-free and cadmium-free CoCr ceramic alloy according to DIN EN OSP 22674 and EN ISO 9693 for applications with thin cross-sections which are exposed to extreme forces. Examples are removable partial dentures, clasps, thin veneered individual crowns, fixed full arch dentures or bridges with small cross-sections, bars, fixations, implant-supported supraconstructions. Properties: Alloy type: 4Density: 8.8 g/cm³Vickers hardness: 285 HV 10/30CTE- value (25-500 °C): 14,4*10-6 K-1Oxidation without vacuum (Point 4c): 1000 °CMass content of the components (in weight-%)*: Co 63, Cr 29, Mo 6 / Mn x, Nb x, Si x, Fe xTensile strength: 680 MPa0.2 % yield point: 400 MPaElongation at break: 9 %E-module: 250 GPa *X= <, 1%
Tizian Blank NEM fine 98 mm
Tizian Blanks NEM (non-precious metal) are made of beryllium-free and cadmium-free CoCr ceramic alloy according to DIN EN OSP 22674 and EN ISO 9693 for applications with thin cross-sections which are exposed to extreme forces. Examples are removable partial dentures, clasps, thin veneered individual crowns, fixed full arch dentures or bridges with small cross-sections, bars, fixations, implant-supported supraconstructions. Properties: Alloy type: 4Density: 8.8 g/cm³Vickers hardness: 285 HV 10/30CTE- value (25-500 °C): 14,4*10-6 K-1Oxidation without vacuum (Point 4c): 1000 °CMass content of the components (in weight-%)*: Co 63, Cr 29, Mo 6 / Mn x, Nb x, Si x, Fe xTensile strength: 680 MPa0.2 % yield point: 400 MPaElongation at break: 9 %E-module: 250 GPa *X= <, 1%
Tizian Blank NEM fine 98 mm
Tizian Blanks NEM (non-precious metal) are made of beryllium-free and cadmium-free CoCr ceramic alloy according to DIN EN OSP 22674 and EN ISO 9693 for applications with thin cross-sections which are exposed to extreme forces. Examples are removable partial dentures, clasps, thin veneered individual crowns, fixed full arch dentures or bridges with small cross-sections, bars, fixations, implant-supported supraconstructions. Properties: Alloy type: 4Density: 8.8 g/cm³Vickers hardness: 285 HV 10/30CTE- value (25-500 °C): 14,4*10-6 K-1Oxidation without vacuum (Point 4c): 1000 °CMass content of the components (in weight-%)*: Co 63, Cr 29, Mo 6 / Mn x, Nb x, Si x, Fe xTensile strength: 680 MPa0.2 % yield point: 400 MPaElongation at break: 9 %E-module: 250 GPa *X= <, 1%
T4/T9 Tizian Cut 5/3.5 Metal Drill CoCr/Ti 1mm, 6 mm shaft
Radius cutter short, double-edged, edge Ø 1 mm, shaft Ø 6 mm, total length 45 mm. Max. blank height = short up to 15 mm, long up to 20 mm. Processing type: fine finishing Blank material: CoCr, titanium Type: coated Coding color: gold For the milling machines: Tizian Cut 5.2, Tizian Cut 5.2 plus, Tizian Cut 5 option metal milling (6 mm shaft), CORiTEC 550i, CORiTEC 650i